Castables Table

CAST 13

CAST 13 ES

CAST 15

CAST 16

CAST 16 ES

Maximum Service Temperature°C1,3001,3001,5001,6001,600
Maximum Grain Size of Aggregates mm.55555
Approximate Weight Required for Castingkg/m32,010 – 2,0202,010 – 2,0202,200 – 2,2102,500 – 2,5302,520 – 2,540
Approximate Amount of Water Required for Casting%10 – 2010 – 1210 – 1210 – 1210 – 12
Bulk Density After Drying at 110°Ckg/m32,050 – 2,0702,110 – 2,0202,250 – 2,2602,350 – 2,3802,350 – 2,400
Cold Crushing Strength After Drying at 110°C kg/cm2350 – 380400 – 450300 – 320380 – 400400 – 450
Modulus of Rupture
– After Drying at 110°Ckg/cm260 – 7070 – 8070 – 7570 – 7570 – 75
– After Heating atkg/cm2(1,260°C)
35 – 40
(1,480°C)
60 – 70
(1,480°C)
80 – 85
(1,480°C)
80 – 85
(1,480°C)
80 – 85
Permanent Linear Change
After Heating at
 %(1,260°C)
+0.5
(1,480°C)
+0.5
 (1,480°C)
-0.5
(1,480°C)
-0.15
(1,480°C)
-0.15

CAST 17 CG

CAST 18

CAST 11 LW

CAST 13 LW

Maximum Service Temperature°C1,7001,8001,1001,300
Maximum Grain Size of Aggregates mm.12.5535
Approximate Weight Required for Castingkg/m32,560 – 2,5802,700 – 2,730800 – 9001,200 – 1,300
Approximate Amount of Water Required for Casting%10 – 2010 – 1240 – 5035
Bulk Density After Drying at 110°Ckg/m32,640 – 2,6502,800 – 2,820900 – 9501,400 – 1,450
Cold Crushing Strength After Drying at 110°C kg/cm2380 – 400490 – 50030 – 40110 – 120
Modulus of Rupture
– After Drying at 110°Ckg/cm280 – 85100 – 1208.020 – 25
– After Heating atkg/cm2(1,480°C)
90 – 100
(1,480°C)
490 – 100
(1,000°C)
4.0
(1,260°C)
40 – 45
Permanent Linear Change
After Heating at
 %(1,480°C)
-0.5
(1,480°C)
-0.18
 (1,000°C)
-0.08
 (1,260°C)
-0.05

C60

C82

ALC90

NEO – 165

Maximum Service Temperature°C1,6001,7001,7501,650
Maximum Grain Size of Aggregates mm.12.512.512.512.5
Approximate Weight Required for Castingkg/m32,400 – 2,4302,800 – 2,8503,150 – 3,2002,650
Approximate Amount of Water Required for Casting%5.0 – 5.55.0 – 5.54.0 – 4.55.0
Bulk Density After Drying at 110°Ckg/m32,430 – 2,4402,840 – 2,8603,1502,760
Cold Crushing Strength After Drying at 110°C kg/cm2520 – 550340 – 350300 – 35080 – 90
Modulus of Rupture
– After Drying at 110°Ckg/cm260 – 654045625 – 650
Permanent Linear Change
After Heating at 1,400°C
 %-0.50-0.40-0.20 -0.15

CAST 13

CAST 13 ES

CAST 15

CAST 16

CAST 16 ES

Maximum Service Temperature°C1,3001,3001,5001,6001,600
Maximum Grain Size of Aggregates mm.55555
Approximate Weight Required for Castingkg/m32,010 – 2,0202,010 – 2,0202,200 – 2,2102,500 – 2,5302,520 – 2,540
Approximate Amount of Water Required for Casting%10 – 2010 – 1210 – 1210 – 1210 – 12
Bulk Density After Drying at 110°Ckg/m32,050 – 2,0702,110 – 2,0202,250 – 2,2602,350 – 2,3802,350 – 2,400
Cold Crushing Strength After Drying at 110°C kg/cm2350 – 380400 – 450300 – 320380 – 400400 – 450
Modulus of Rupture
– After Drying at 110°Ckg/cm260 – 7070 – 8070 – 7570 – 7570 – 75
– After Heating atkg/cm2(1,260°C)
35 – 40
(1,480°C)
60 – 70
(1,480°C)
80 – 85
(1,480°C)
80 – 85
(1,480°C)
80 – 85
Permanent Linear Change
After Heating at
 %(1,260°C)
+0.5
(1,480°C)
+0.5
 (1,480°C)
-0.5
(1,480°C)
-0.15
(1,480°C)
-0.15

CAST 17 CG

CAST 18

CAST 11 LW

CAST 13 LW

Maximum Service Temperature°C1,7001,8001,1001,300
Maximum Grain Size of Aggregates mm.12.5535
Approximate Weight Required for Castingkg/m32,560 – 2,5802,700 – 2,730800 – 9001,200 – 1,300
Approximate Amount of Water Required for Casting%10 – 2010 – 1240 – 5035
Bulk Density After Drying at 110°Ckg/m32,640 – 2,6502,800 – 2,820900 – 9501,400 – 1,450
Cold Crushing Strength After Drying at 110°C kg/cm2380 – 400490 – 50030 – 40110 – 120
Modulus of Rupture
– After Drying at 110°Ckg/cm280 – 85100 – 1208.020 – 25
– After Heating atkg/cm2(1,480°C)
90 – 100
(1,480°C)
490 – 100
(1,000°C)
4.0
(1,260°C)
40 – 45
Permanent Linear Change
After Heating at
 %(1,480°C)
-0.5
(1,480°C)
-0.18
 (1,000°C)
-0.08
 (1,260°C)
-0.05

C60

C82

ALC90

NEO – 165

Maximum Service Temperature°C1,6001,7001,7501,650
Maximum Grain Size of Aggregates mm.12.512.512.512.5
Approximate Weight Required for Castingkg/m32,400 – 2,4302,800 – 2,8503,150 – 3,2002,650
Approximate Amount of Water Required for Casting%5.0 – 5.55.0 – 5.54.0 – 4.55.0
Bulk Density After Drying at 110°Ckg/m32,430 – 2,4402,840 – 2,8603,1502,760
Cold Crushing Strength After Drying at 110°C kg/cm2520 – 550340 – 350300 – 35080 – 90
Modulus of Rupture
– After Drying at 110°Ckg/cm260 – 654045625 – 650
Permanent Linear Change
After Heating at 1,400°C
 %-0.50-0.40-0.20 -0.15