Ramming & Gunning Mixes

Ramming & Gunning Mixes

GUNNING MIXES M 85

CLASSIFICATION : MAGNESITE BASE GUNNING MIXES
PRODUCT INFORMATION:

  • Maximum Service Temperature 1,800 ° C
    Maximum Grain Size of Aggregates 4 mm.
    Approximate Amount of Water 10 – 15 %
    Required for Gunning
    Approximate Weight Requiring for forming 2,280 kg / m3
    Cold Crushing Strength
    After Drying at 110 ° C 300 – 350 kg / cm2
    After Heating at 1,200 ° C 200 – 250 kg / cm2
    Permanent Linear Change
    After Drying at 110 ° C – 0.05 kg / cm2
    After Heating at 1,200 ° C – 0.10 kg / cm2

  • Silica (SiO2) 5.2 %
    Alumina (Al2O3) 1.5 %
    Iron Oxide (Fe2O3) 2.1 %
    Magnesium Oxide (MgO) 84.1 %
    Calcium Oxide (CaO) 1.5 %

GUNNING MIXES M 92

CLASSIFICATION : CHEMICAL BONDED HIGH PURITY MAGNESITE GUNNING MIXES
PRODUCT INFORMATION:

  • Maximum Service Temperature 1,800 ° C
    Maximum Grain Size of Aggregates 4 mm.
    Approximate Amount of Water 10-15 %
    Required for Gunning
    Approximate Weight Requiring for Ramming 2,300 kg / m3
    Cold Crushing Strength
    After Drying at 110 ° C 300 – 350 kg / cm2
    After Heating at 1,200 ° C 200 – 250 kg / cm2
    Permanent Linear Change
    After Drying at 110 ° C – 0.05 kg / cm2
    After Heating at 1,200 ° C – 0.10 kg / cm2

  • Silica (SiO2) 2.5 %
    Alumina (Al2O3) 1.2 %
    Iron Oxide (Fe2O3) 2.1 %
    Magnesium Oxide (MgO) 91.8 %
    Calcium Oxide (CaO) 1.8 %

RAMMING MIXES M 95

CLASSIFICATION : CHEMICAL – BONDED MAGNESITE RAMMING MIXES
PRODUCT INFORMATION:

  • Maximum Service Temperature 1,800 ° C
    Maximum Grain Size of Aggregates 5 mm.
    Approximate Amount of Water Required for 8 – 15 litres
    Ramming Per 50 kgs.
    Approximate Weight Requiring for Ramming 2,800 kg / m3
    Cold Crushing Strength
    After Drying at 110 ° C 300 – 350 kg / cm2
    After Heating at 1,200 ° C 200 – 250 kg / cm2
    Permanent Linear Change
    After Drying at 110 ° C – 0.05 kg / cm2
    After Heating at 1,200 ° C – 0.10 kg / cm2

  • Silica (SiO2) 3.1 %
    Alumina (Al2O3) 1.4 %
    Iron Oxide (Fe2O3) 2.1 %
    Magnesium Oxide (MgO) 93.2 %
    Calcium Oxide (CaO) 1.5 %