Plastic 43 | Plastic 60 | ||
---|---|---|---|
Maximum Service Temperature | °C | 1,700 | 1,760 |
Approximate Amount Required as Rammed | kg/m3 | 2,300 – 2,400 | 2,550 – 2,560 |
Bulk Density After Drying at 110°C | kg/m3 | 2,150 – 2,200 | 2,390 – 2,400 |
Modulus of Rupture | |||
– After Drying at 110°C | kg/cm2 | 5 – 8 | 5 – 8 |
– After Heating at 1,200°C | kg/cm2 | 40 – 45 | 55 – 60 |
Permanent Linear Change | |||
– After Drying at 110°C | kg/cm2 | -0.8 | -0.8 |
– After Heating at 1,200°C | kg/cm2 | -0.3 | -0.1 |