Mortar 30 HM | Mortar 43 HM | Mortar 70 HM | MA 95 HM | ||
---|---|---|---|---|---|
Maximum Service Temperature | °C | 1750 | |||
Pyrometric Cone Equivalent | Orton Cone | 30 | 33 – 34 | 37 – 38 | >38 |
Approximate Amount of Water for Trowelling Consistency | Litres/50kg | 20 – 25 | 20 – 25 | 18 – 20 | 10 – 11 |
Approximate Amount Required Per 1,000 pcs 9″ Standard Brick Equivalent Thinly Trowelled Joints | kg | 160 – 180 | 150 – 200 | 150 – 200 | 220 – 230 |
Modulus of Rupture After Drying at 110 °C | kg/cm2 | 20 | 21 | 23 |
Mortar 30 AM | Mortar 43 AM | Mortar SK 38 PM | ||
---|---|---|---|---|
Refractoriness | Orton Cone | 30 | 33 – 34 | 38 |
Approximate Amount Required Per 1,000 pcs 9″ Standard Brick Equivalent Thinly Trowelled Joints | kg | 200 – 250 | 200 – 210 | 220 – 225 |
Modulus of Rupture After Drying at 110 °C | kg/cm2 | 25 | 25 | 35 |
Mortar 30 HM | Mortar 43 HM | Mortar 70 HM | MA 95 HM | ||
---|---|---|---|---|---|
Maximum Service Temperature | °C | 1750 | |||
Pyrometric Cone Equivalent | Orton Cone | 30 | 33 – 34 | 37 – 38 | >38 |
Approximate Amount of Water for Trowelling Consistency | Litres/50kg | 20 – 25 | 20 – 25 | 18 – 20 | 10 – 11 |
Approximate Amount Required Per 1,000 pcs 9″ Standard Brick Equivalent Thinly Trowelled Joints | kg | 160 – 180 | 150 – 200 | 150 – 200 | 220 – 230 |
Modulus of Rupture After Drying at 110 °C | kg/cm2 | 20 | 21 | 23 |
Mortar 30 AM | Mortar 43 AM | Mortar SK 38 PM | ||
---|---|---|---|---|
Refractoriness | Orton Cone | 30 | 33 – 34 | 38 |
Approximate Amount Required Per 1,000 pcs 9″ Standard Brick Equivalent Thinly Trowelled Joints | kg | 200 – 250 | 200 – 210 | 220 – 225 |
Modulus of Rupture After Drying at 110 °C | kg/cm2 | 25 | 25 | 35 |